HOME » Knowledge » 0.5mm aluminium coil 3003

0.5mm aluminium coil 3003


0.5mm aluminium coil 3003  H14 is definitely the most extensively utilised aluminum alloy. It is produced up of aluminum, copper, iron, manganese, silicon and zinc. It is actually usually utilized because it has great resistance to corrosion and is moderately robust. The 3003 aluminum coil is 20% stronger than 1100 grade alloys since it is fused with manganese.

Due to the fact it?ˉs not heat treatable, it must be strengthened employing cold working alone.

By far the most widespread applications for the 0.5mm aluminium coil 3003 are for fuel tanks, sheet metal perform and other kinds of projects that will need a metal which is stronger than the 1100 series aluminum. In some situations, it’s applied for cooking utensils, refrigerator panels, gas lines, storage tanks, garage doors, builder?ˉs hardware and awning slats.

The machinability of the 0.5mm aluminium coil 3003 H14 is thought of great for being an aluminum alloy. It’s readily machined for the unique applications. It could either be formed applying traditional hot operating or cold working. It?ˉs also attainable to make use of conventional welding methods to shape 3003 aluminum. It really is often welded to other aluminum alloys, like 6061, 5052 and 6062, which must have an AL 4043 filler rod.

0.5mm aluminium coil 3003 isn?ˉt heat treatable, nevertheless it can be forged with heat that?ˉs between 500 and 950 degrees Fahrenheit. When making use of heat within this range, the aluminum is often hot worked easily. However, it is readily cold worked, which can be carried out working with traditional procedures. When annealing the alloy for the duration of or just after using cold functioning tactics, it must be performed at 775 degrees Fahrenheit. This will likely give it enough time to completely heat ahead of becoming air cooled. The only way to make this alloy challenging is together with the use of cold operating. It can also be deep drawn, spun or brazed.

Tensile Strength
(PSI) Yield Strength
(PSI) Elongation
% in 2??
.064 Sheet Min 90?? Cold
Bend Radius for
.64?? Thick
3003-O 16,000 6,000 30 0
3003-H 12 19,000 18,000 10 0
3003-H 14 22,000 21,000 8 0
3003-H 16 26,000 25,000 5 1/2-1 1/2 T
3003-H 18 29,000 27,000 4 1 1/2 ¨C 3 T
If you want to understand much more specifics about 0.5mm aluminium coil 3003 H14,pls inform us !E-mail: demi@jianhuimetals.com