The temper designation follows the aluminum Al Alloy sheets code and is separated by a hyphen.
-F As Fabricated: Applies to products of rolling or forming where there is no special control over the thermal or work-hardening conditions. Since mechanical properties may vary widely, no limits have been assigned. This temper usually applies to sheet products which are at intermediate stages of production.
-H Strain-Hardened: Applies to wrought products which are strengthened by cold-rolling or cold-working.
-O Annealed: Applies to wrought products which have been heated above the recrystallization temperature to produce the lowest tensile strength condition of the alloy.
Average1 | Thermal | Electrical Conductivity at 68°F | Electrical | |||||
Coeffecient of | Melting | (Percent of International | Resistivity | |||||
Thermal | Conductivity | Annealed Copper Standard) | at 68°F | |||||
Expansion | Range 2,3 | Density | (English | (Ohms-Cir. | ||||
Alloy | Equal | Equal | ||||||
68° to 212°F | Approximately | (lbs/cubic in.) | Units4) | Mil/Foot) | ||||
(°F) | (°F) | Volume | Volume | |||||
1100 | 13.1 | 1190-1215 | 0.098 | 1520 | 59 | 194 | 18 | |
1350 | 13.2 | 1195-1215 | 0.0975 | 1625 | 62 | 204 | 17 | |
2024-O | 12.9 | 935-11805 | 0.100 | 1340 | 50 | 160 | 21 | |
2024-T3,T4 | 12.9 | 935-11805 | 0.100 | 840 | 30 | 96 | 35 | |
2024-T6 | 12.9 | 935-11805 | 0.100 | 1050 | 38 | 122 | 27 | |
3003 | 12.9 | 1190-1210 | 0.099 | 1200 | 48 | 156 | 22 | |
3004 | 13.3 | 1165-1210 | 0.098 | 1100 | 41 | 134 | 25 | |
3005 | 13.1 | 1175-1210 | 0.098 | 1190 | 45 | 148 | 23 | |
5005 | 13.2 | 1170-1210 | 0.098 | 1390 | 52 | 172 | 20 | |
5050 | 13.2 | 1155-1205 | 0.097 | 1340 | 50 | 165 | 21 | |
5052 | 13.2 | 1125-1200 | 0.097 | 960 | 35 | 116 | 30 | |
5056 | 13.4 | 1055-1180 | 0.096 | 790 | 28 | 95 | 37 | |
5182 | 13.4 | 1055-1180 | 0.096 | 790 | 28 | 95 | 37 | |
5657 | 13.2 | 1180-1215 | 0.097 | 960 | 35 | 116 | 30 | |
6061-O | 13.1 | 1080-12056 | 0.098 | 1250 | 47 | 155 | 22 | |
6061-T4 | 13.1 | 1080-12056 | 0.098 | 1070 | 40 | 132 | 26 | |
6061-T6 | 13.1 | 1080-12056 | 0.098 | 1160 | 43 | 142 | 24 |
Material properties such as light weight combined with high strength and resistance to corrosion contribute to low environmental loading. After iron, aluminium is now the second most widely used metal in the world.
This is because aluminum Al Alloy sheets has a unique combination of attractive properties:
• Low weight
• High strength
• Superior malleability
• Easy machining
• Excellent corrosion resistance
• Easy to mill, drill, cut, punch, bend, weld, bond, tape…
if you want to know more about aluminum Al Alloy sheets, pls feel free to tell me.