HOME » Knowledge » where to get aluminum alloy 3003-0

where to get aluminum alloy 3003-0


Aluminum alloy 3003-0 could be the most widely applied aluminum alloy. It can be made up of aluminum, copper, iron, manganese, silicon and zinc. It truly is generally made use of because it has terrific resistance to corrosion and is moderately powerful. The 3003 aluminum coil is 20% stronger than 1100 grade alloys since it is fused with manganese.

Since it?ˉs not heat treatable, it must be strengthened making use of cold working alone.

One of the most prevalent applications for the Aluminum alloy 3003-0 are for fuel tanks, sheet metal work and also other kinds of projects that need to have a metal that is definitely stronger than the 1100 series aluminum. In some circumstances, it truly is utilised for cooking utensils, refrigerator panels, gas lines, storage tanks, garage doors, builder?ˉs hardware and awning slats.

The machinability of the 3003 Aluminum coil H14 is regarded good for becoming an aluminum alloy. It is readily machined for the distinctive applications. It may either be formed utilizing conventional hot functioning or cold operating. It?ˉs also probable to work with standard welding strategies to shape 3003 aluminum. It truly is in some cases welded to other aluminum alloys, like 6061, 5052 and 6062, which must have an AL 4043 filler rod.

Aluminum alloy 3003-0 isn?ˉt heat treatable, nevertheless it can be forged with heat that?ˉs among 500 and 950 degrees Fahrenheit. When using heat in this variety, the aluminum may be hot worked conveniently. On the other hand, it can be readily cold worked, which is usually carried out applying conventional solutions. When annealing the alloy during or right after making use of cold functioning techniques, it must be performed at 775 degrees Fahrenheit. This will likely give it enough time to completely heat prior to getting air cooled. The only solution to make this alloy difficult is together with the use of cold functioning. It might also be deep drawn, spun or brazed.

Tensile Strength
(PSI) Yield Strength
(PSI) Elongation
% in 2??
.064 Sheet Min 90?? Cold
Bend Radius for
.64?? Thick
Aluminum alloy 3003-0 O 16,000 6,000 30 0
3003-H 12 19,000 18,000 10 0
3003-H 14 22,000 21,000 8 0
3003-H 16 26,000 25,000 5 1/2-1 1/2 T
3003-H 18 29,000 27,000 4 1 1/2 ¨C three T
If you want to understand much more details about 3003 aluminum coil H14,pls tell us !E mail:demi@jianhuimetals.com